Kikuchi A., Iijima Y., Iijima Y., Ohuchi N., Tsuchiya K., Takao T., Wang X., Fujita S., Terashima A., Suzuki K., Tawada M., Daibo M., Masuzawa M., Norimoto K.
Ключевые слова: HTS, coated conductors, commercialization, helium, nitrogen liquid , critical caracteristics, YBCO, GdBCO, REBCO, comparison, IBAD process, PLD process, RCE-LATS process, MOCVD process, substrate Hastelloy, stabilizing layers, Cu-based conductors, critical current, n-value, magnetic field dependence, angular dependence, experimental results
Ключевые слова: HTS, coated conductors, YBCO, GdBCO, YGdBCO, microstructure, phase composition, pinning, comparison, commercialization, MOD process, MOCVD process, PLD process, RCE-LATS process, IBAD process, RABITS process, X-ray diffraction, critical caracteristics, Jc/B curves, anisotropy, pinning force, experimental results
Ключевые слова: HTS, GdBCO, coated conductors, Al, alloys, laminations, solder, reinforcement, RCE-LATS process, critical caracteristics, current-voltage characteristics, fabrication
Ключевые слова: HTS, coated conductors, cable-in-conduit conductor, critical caracteristics, comparison, commercialization, geometry effects, MOD process, MOCVD process, PLD process, RCE-LATS process, IBAD process, RABITS process, critical current, magnetic field dependence, temperature dependence, critical current density, magnetic flux distribution, experimental results
Ключевые слова: HTS, YBCO, coated conductors, fabrication, IBAD process, template layers, RCE-CDR process, economic analysis, RCE-LATS process, review
© Copyright 2006-2012. Использование материалов сайта возможно только с обязательной ссылкой на сайт.
Свои замечания и пожелания вы можете направлять по адресу perst@isssph.kiae.ru
Техническая поддержка Alexey, дизайн Teodor.